Stainless steel plate is a general term for stainless steel plate and acid-resistant steel plate. Stainless steel plate refers to the steel plate that is resistant to corrosion by weak media such as atmosphere, steam and water, while acid-resistant steel plate refers to the steel plate that is resistant to corrosion by chemically leaching media such as acid, alkali and salt.
|
Product |
Stainless Steel Plate,stainless steel sheet,metal sheet |
|
Standard&Grade |
GB/T14976-2002, GB13296-91, GB9948-88, ASTM/ASME A213/SA213, ASTM/ASME A312/SA312, ASTM/ASME A269/SA269, DIN 17458-85,DIN 17456-85, JIS G 3459, JIS G 3463, JIS G 3448, JIS G 344 |
|
Size |
Sheet(0.2mm-4mm), Slab(4mm-20mm), Thick plate(20mm-60mm), Special thick plate(60-115mm) |
|
Tolerance |
Outer Diameter:6-32mm:+/- 0.2mm, 32-38:+/-0.15mm,42-60:+/-0.20mm,60mm:+/-0.25mm b) Thickness: +/- 10% c) Length: +/- 5mm |
|
Industrial process |
Hot rolled,hot expanded,cold drawn,and hot galvanized |
|
Surface |
180G, 240G, 320G Satin / Hairline,400G, 600G Mirror finish |
310/ 310S stainless steel sheet
|
310 stainless steel Austenitic chromium-nickel steel has good oxidation resistance, corrosion resistance, because the higher percentage of chromium and nickel, 310 has much better creep strength, can continuously work under high temperature, good heat resistance. |
|||||||
|
310S stainless steel is Austenitic chromium-nickel steel, has a good 310S stainless steel oxidation resistance, resistance Corrosive. |
|||||||
|
The differences of chemical composition for 310/310S stainless steel |
|||||||
|
Grade |
C(%) |
Si(%) |
Mn(%) |
P(%) |
S(%) |
Cr(%) |
Ni(%) |
|
310 |
≤0.25 |
≤1.0 |
≤2.0 |
≤0.03 |
— |
24.0-26.0 |
19.0-22.0 |
|
310S |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.03 |
≤0.03 |
24.0-26.0 |
19.0-22.0 |
|
The differences of Mechanical property for 310/310S stainless steel |
|||||||
|
Grade |
Tensile Strength Mpa |
Yield Strength Mpa |
Elongation (%) |
Rate of Reduction in Area(%) |
Density (g/cm3) |
|
|
|
310 |
≥470 |
≥17 |
≥40 |
≥50 |
7.98 |
|
|
|
310S |
≥520 |
≥205 |
≥40 |
≥50 |
7.98 |
|
|
|
304/ 304L/ 304H stainless sheet |
|||||||||
|
304 stainless steel is a common stainless steel material, the density of 7.93 g/cm3, the industry is also called 18/8 stainless steel. High temperature resistance of 800 degrees, with good processing performance, high toughness characteristics, widely used in industrial and furniture decoration industry and food industry. |
|||||||||
|
304L steel as a low C in the general state, its corrosion resistance and 304 similar, but after welding or stress after its excellent corrosion resistance to the grain boundary. In the case without heat treatment, can remain good corrosion resistance, generally use 400 or less (non-magnetic, temperature -196 degrees Celsius to 800 degrees Celsius). Widely used to produce good overall performance requirements (corrosion resistance and formability) of equipment and parts. |
|||||||||
|
304H is a kind of stainless steel, with good bending, welding process performance, corrosion resistance, high durability and organizational stability, cold deformation ability is very good. The highest temperature can reach 650 DEG C, and the oxidation resistance is up to 850 DEG C |
|||||||||
|
The differences of Chemical composition for 304 304L 304H |
|||||||||
|
Grade |
C(%) |
Si(%) |
Mn(%) |
P(%) |
S(%) |
Cr(%) |
Ni(%) |
||
|
304 |
≤0.08 |
≤0.75 |
≤2.0 |
≤0.045 |
≤0.03 |
18.0-20.0 |
8.0-10.5 |
||
|
304L |
≤0.03 |
≤0.75 |
≤2.0 |
≤0.045 |
≤0.03 |
18.0-20.0 |
8.0-12.0 |
||
|
304H |
0.04-1.0 |
≤0.75 |
≤2.0 |
≤0.045 |
≤0.03 |
18.0-20.0 |
8.0-10.5 |
||
|
The differences of Mechanical property for 304 304L 304H |
|||||||||
|
Grade |
Tensile Strength (Mpa) |
Yield Strength (Mpa) |
Elongation (%) |
Hardness (HR) |
|||||
|
304 |
≥515 |
≥205 |
≥40 |
≥92 |
|||||
|
304L |
≥485 |
≥170 |
≥40 |
≥92 |
|||||
|
304H |
≥515 |
≥205 |
≥40 |
≥92 |
|||||
|
|
|||||||||
|
316/ 316L stainless steel sheet |
|||||||||
|
316 stainless steel by adding Mo element, the corrosion resistance, and high temperature strength has greatly improved, high temperature can reach 1200-1300 degrees, can be used in severe conditions.Corrosion resistance is better than 304 stainless steel, in pulp and paper production process has good corrosion resistance. And 316 stainless steel is also resistant to erosion of marine and corrosive industrial atmosphere. |
|||||||||
|
316L stainless steel has a carbon content of less than 316, which is commonly used in pulp and paper equipment heat exchangers, dyeing equipment, film washing equipment, pipelines, coastal areas outside the building materials. Corrosion resistance is better than 316 material. |
|||||||||
|
The differences of chemical composition for 316 316L stainless steel |
|||||||||
|
Grade |
C(%) |
Si(%) |
Mn(%) |
P(%) |
S(%) |
Cr(%) |
Ni(%) |
Mo(%) |
|
|
316 |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.045 |
≤0.03 |
16.0-18.0 |
10.0-14.0 |
2.0-3.0 |
|
|
316L |
≤0.03 |
≤1.0 |
≤2.0 |
≤0.045 |
≤0.03 |
16.0-18.0 |
10.0-14.0 |
2.0-3.0 |
|
|
The differences of Mechanical property for 316 316L stainless steel |
|||||||||
|
Grade |
Tensile StrengthMpa |
Yield StrengthMpa |
Elongation(%) |
Rate of Reduction in Area(%) |
Density (g/cm3) |
||||
|
316 |
≥520 |
≥205 |
≥40 |
≥60 |
7.98 |
||||
|
316L |
≥480 |
≥177 |
≥40 |
≥60 |
7.98 |
||||
|
430 stainless steel sheet |
|||||||||
|
430 stainless steel is a good corrosion resistance of common steel, thermal performance than austenitic good, thermal expansion coefficient than austenitic small, heat fatigue, add stabilization element titanium, weld parts mechanical performance is good. |
|||||||||
|
430 stainless steel used in architectural use, fuel burner parts, household appliances, home appliance parts. |
|||||||||
|
Chemical composition for 430 stainelss steel |
|||||||||
|
Grade |
C(%) |
Mn(%) |
Si(%) |
P(%) |
S(%) |
Cr(%) |
Ni(%) |
Mo(%) |
|
|
430 |
≤0.12 |
≤1.0 |
≤0.75 |
≤0.04 |
≤0.03 |
16.0-18.0 |
≤0.06 |
— |
|
|
Mechanical property for 430 stainless steel |
|
|
|||||||
|
Grade |
Tensile StrengthMpa |
Yield StrengthMpa |
Elongation(%) |
Rate of Reduction in Area(%) |
Density (g/cm3) |
|
|
|
|
|
430 |
≥450 |
≥205 |
≥22 |
— |
7.75 |
|
|
|
|